| Product | Mixed Viscocity | Mixed Viscocity | Cure Time | Shore A Hardness | Specific Gravity | Specific Volume | Color | Tensile Strength | Die C Tear Strength | Elongation At Break | Thin Film Recoat Time | Tack Free Time | Hundred Percent Modulus | Mix Ratio By Weight | Pot Life | Hundred Percent Modulus | Color | Cure Time | Pot Life | Specific Volume | Die C Tear Strength | Specific Gravity | Mix Ratio By Weight | Tack Free Time | Tensile Strength | Elongation At Break | Shore A Hardness | Thin Film Recoat Time |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| UreCoat™ Matting Powder | – | – | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - |
| UreCoat™ | 3,800 cps | 3,800 cps | 16 h. | 70 | 1.05 g/cc | 26.4 cu. in./lb. | Translucent Amber | 1,360 psi | 256 pli | 876 % | 30 min. | 2 h. | 503 psi | 100A:10B | 8 min. | 503 psi | Translucent Amber | 16 h. | 8 min. | 26.4 cu. in./lb. | 256 pli | 1.05 g/cc | 100A:10B | 2 h. | 1,360 psi | 876 % | 70 | 30 min. |