De TASK™ Serie biedt sterke urethaan gietharsen voor duurzame, gedetailleerde onderdelen. Met lage krimp en verschillende verwerkingstijden zijn ze ideaal voor prototypes en functionele componenten.

Beschikbaar in TASK™ Serie

Product	Cure Time	Specific Gravity	Specific Volume	Color	Tensile Strength	Tensile Modulus	Compressive Strength	Compressive Modulus	Flexural Strength	Shrinkage	Heat Deflection Temp	Elongation At Break	Flexural Modulus	Mixed Viscocity	Mix Ratio By Volume	Mix Ratio By Weight	Pot Life	Shore D Hardness	Color	Mixed Viscocity	Cure Time	Pot Life	Flexural Strength	Flexural Modulus	Specific Volume	Specific Gravity	Mix Ratio By Weight	Shrinkage	Mix Ratio By Volume	Tensile Strength	Elongation At Break	Shore D Hardness	Heat Deflection Temp	Compressive Strength	Tensile Modulus	Compressive Modulus	Handling Time	Handling Time	Heat Deflection With Post Cure	Heat Deflection With Post Cure	Shore A Hardness	Die C Tear Strength	Hundred Percent Modulus	Hundred Percent Modulus	Die C Tear Strength	Shore A Hardness
TASK™ 2	60 min.	1.12 g/cc	24.7 cu. in./lb.	White	6,650 psi	290,000 psi	8,300 psi	78,000 psi	9,500 psi	0.005 in. / in.	134 °F	6 %	288,000 psi	150 cps	1A:1B	115A:100B	7 min.	80	White	150 cps	60 min.	7 min.	9,500 psi	288,000 psi	24.7 cu. in./lb.	1.12 g/cc	115A:100B	0.005 in. / in.	1A:1B	6,650 psi	6 %	80	134 °F	8,300 psi	290,000 psi	78,000 psi	-	-	-	-	-	-	-	-	-	-
TASK™ 3	90 min.	1.12 g/cc	24.7 cu. in./lb.	White	6,650 psi	290,000 psi	8,300 psi	78,000 psi	9,500 psi	0.0025 in. / in.	134 °F	6 %	288,000 psi	150 cps	1A:1B	115A:100B	20 min.	80	White	150 cps	90 min.	20 min.	9,500 psi	288,000 psi	24.7 cu. in./lb.	1.12 g/cc	115A:100B	0.0025 in. / in.	1A:1B	6,650 psi	6 %	80	134 °F	8,300 psi	290,000 psi	78,000 psi	-	-	-	-	-	-	-	-	-	-
TASK™ 4	16 h.	1.167 g/cc	23.9 cu. in./lb.	Ivory	6,500 psi	130,000 psi	7,400 psi	75,000 psi	9,000 psi	0.0035 in. / in.	110 °F	4 %	204,000 psi	250 cps	-	100A:100B	20 min.	83	Ivory	250 cps	16 h.	20 min.	9,000 psi	204,000 psi	23.9 cu. in./lb.	1.167 g/cc	100A:100B	0.0035 in. / in.	-	6,500 psi	4 %	83	110 °F	7,400 psi	130,000 psi	75,000 psi	-	-	-	-	-	-	-	-	-	-
TASK™ 5	24 h.	1.1 g/cc	25.2 cu. in./lb.	Tan	4,530 psi	200,000 psi	6,700 psi	83,000 psi	6,480 psi	0.007 in. / in.	145 °F	5 %	216,000 psi	600 cps	1A:1B	1A:1B	3 min.	77	Tan	600 cps	24 h.	3 min.	6,480 psi	216,000 psi	25.2 cu. in./lb.	1.1 g/cc	1A:1B	0.007 in. / in.	1A:1B	4,530 psi	5 %	77	145 °F	6,700 psi	200,000 psi	83,000 psi	15 min.	15 min.	-	-	-	-	-	-	-	-
TASK™ 6	24 h.	1.07 g/cc	25.9 cu. in./lb.	Tan	5,200 psi	146,000 psi	5,570 psi	65,000 psi	6,200 psi	0.0031 in. / in.	162 °F	4 %	182,500 psi	800 cps	1A:1B	1A:1B	7 min.	75	Tan	800 cps	24 h.	7 min.	6,200 psi	182,500 psi	25.9 cu. in./lb.	1.07 g/cc	1A:1B	0.0031 in. / in.	1A:1B	5,200 psi	4 %	75	162 °F	5,570 psi	146,000 psi	65,000 psi	75 min.	75 min.	-	-	-	-	-	-	-	-
TASK™ 7	10 min.	1.2 g/cc	23.1 cu. in./lb.	Off-White	3,390 psi	150,700 psi	5,140 psi	57,600 psi	5,450 psi	0.0111 in. / in.	131 °F	15.1 %	148,900 psi	200 cps	1A:1B	104A:100B	2.5 min.	73	Off-White	200 cps	10 min.	2.5 min.	5,450 psi	148,900 psi	23.1 cu. in./lb.	1.2 g/cc	104A:100B	0.0111 in. / in.	1A:1B	3,390 psi	15.1 %	73	131 °F	5,140 psi	150,700 psi	57,600 psi	-	-	-	-	-	-	-	-	-	-
TASK™ 8	15 min.	1.09 g/cc	25.4 cu. in./lb.	Off-White	5,840 psi	246,000 psi	8,760 psi	77,400 psi	8,280 psi	0.01 in. / in.	194 °F	4 %	271,000 psi	100 cps	1A:1B	120A:100B	2.5 min.	80	Off-White	100 cps	15 min.	2.5 min.	8,280 psi	271,000 psi	25.4 cu. in./lb.	1.09 g/cc	120A:100B	0.01 in. / in.	1A:1B	5,840 psi	4 %	80	194 °F	8,760 psi	246,000 psi	77,400 psi	-	-	263 °F	263 °F	-	-	-	-	-	-
TASK™ 11	16 h.	1.12 g/cc	24.7 cu. in./lb.	Translucent White	2,500 psi	-	-	-	-	0.0024 in. / in.	-	100 %	-	2,000 cps	-	100A:100B	20 min.	60	Translucent White	2,000 cps	16 h.	20 min.	-	-	24.7 cu. in./lb.	1.12 g/cc	100A:100B	0.0024 in. / in.	-	2,500 psi	100 %	60	-	-	-	-	-	-	-	-	-	-	-	-	-	-
TASK™ 12	16 h.	1.08 g/cc	26 cu. in./lb.	Clear Amber	2,700 psi	-	-	-	-	0.001 in. / in.	-	300 %	-	2,400 cps	-	100A:44B	20 min.	60	Clear Amber	2,400 cps	16 h.	20 min.	-	-	26 cu. in./lb.	1.08 g/cc	100A:44B	0.001 in. / in.	-	2,700 psi	300 %	60	-	-	-	-	-	-	-	-	-	-	-	-	-	-
TASK™ 13	20 min.	1.15 g/cc	24.1 cu. in./lb.	Black	1,800 psi	-	-	-	-	0.005 in. / in.	-	125 %	-	800 cps	-	100A:120B	3 min.	50	Black	800 cps	20 min.	3 min.	-	-	24.1 cu. in./lb.	1.15 g/cc	100A:120B	0.005 in. / in.	-	1,800 psi	125 %	50	-	-	-	-	-	-	-	-	-	-	-	-	-	-
TASK™ 14	45 min.	1.15 g/cc	24.1 cu. in./lb.	Black	1,800 psi	-	-	-	-	0.0035 in. / in.	-	125 %	-	800 cps	-	100A:120B	10 min.	50	Black	800 cps	45 min.	10 min.	-	-	24.1 cu. in./lb.	1.15 g/cc	100A:120B	0.0035 in. / in.	-	1,800 psi	125 %	50	-	-	-	-	-	-	-	-	-	-	-	-	-	-
TASK™ 15	1 h.	1.12 g/cc	24.7 cu. in./lb.	Opaque White	2,720 psi	126,000 psi	5,450 psi	60,000 psi	5,450 psi	0.0042 in. / in.	117 °F	20 %	170,000 psi	600 cps	-	75A:100B	6 min.	75	Opaque White	600 cps	1 h.	6 min.	5,450 psi	170,000 psi	24.7 cu. in./lb.	1.12 g/cc	75A:100B	0.0042 in. / in.	-	2,720 psi	20 %	75	117 °F	5,450 psi	126,000 psi	60,000 psi	-	-	-	-	-	-	-	-	-	-
TASK™ 16	24 h.	1.08 g/cc	25.64 cu. in./lb.	Light Yellow	2,264 psi	-	-	-	-	0.0025 in. / in.	-	233 %	-	1,400 cps	-	1A:2B	6 min.	30	Light Yellow	1,400 cps	24 h.	6 min.	-	-	25.64 cu. in./lb.	1.08 g/cc	1A:2B	0.0025 in. / in.	-	2,264 psi	233 %	30	-	-	-	-	90 min.	90 min.	-	-	80	197 pli	855 psi	855 psi	197 pli	80
TASK™ 18	16 h.	1.57 g/cc	17.6 cu. in./lb.	Metal Gray	3,250 psi	514,000 psi	8,420 psi	97,300 psi	10,700 psi	0.0006 in. / in.	149 °F	1 %	86,000 psi	4,400 cps	-	26A:100B	20 min.	88	Metal Gray	4,400 cps	16 h.	20 min.	10,700 psi	86,000 psi	17.6 cu. in./lb.	1.57 g/cc	26A:100B	0.0006 in. / in.	-	3,250 psi	1 %	88	149 °F	8,420 psi	514,000 psi	97,300 psi	-	-	-	-	-	-	-	-	-	-
TASK™ 21	1 h.	1.07 g/cc	25.9 cu. in./lb.	White	5,500 psi	270,000 psi	7,100 psi	78,500 psi	7,100 psi	0.0058 in. / in.	144 °F	7.5 %	250,000 psi	500 cps	2A:1B	2A:1B	6 min.	75	White	500 cps	1 h.	6 min.	7,100 psi	250,000 psi	25.9 cu. in./lb.	1.07 g/cc	2A:1B	0.0058 in. / in.	2A:1B	5,500 psi	7.5 %	75	144 °F	7,100 psi	270,000 psi	78,500 psi	-	-	-	-	-	-	-	-	-	-

Waarom kopen bij FormX?

Wij houden van materiaal

Al ruim dertig jaar zoeken we wereldwijd naar de beste materialen voor modelleren, mallen maken en gieten.
Inspirerend + Uniek

Van siliconen en harsen tot Jesmonite en special effects-materialen — een zorgvuldig samengesteld assortiment voor professionals, kunstenaars en makers.
Deskundig advies

Ons salesteam staat bekend om hun kennis en betrokkenheid en helpt je graag bij mallen maken, gieten, beeldhouwen en prototyping.
Verzending door heel Europa

We verzenden vanuit onze magazijnen in Amsterdam, Barcelona en Madrid naar klanten in heel Europa, van Griekenland tot Noorwegen.
Amsterdams origineel

Opgericht in Amsterdam groeide FormX van een lokale kunstgieterij uit tot een grote Europese leverancier — met onze wortels stevig in de stad.

FormX is gespecialiseerd in de levering en gespecialiseerde handel in 3D-modelleermaterialen in de breedste zin van het woord en heeft magazijnen en showrooms in Amsterdam, Barcelona en Madrid.

Legal

Webwinkel

Over

Community

Deze website is ontwikkeld door Usecue B.V.
© 2026 FormX B.V.