Simpact™ 60A

Simpact60ax ⓘ 6EF5A536-BF1A-2C45-A855-8BCC11B16688
Polyurethane Elastomer
exclamation.svg health-hazard.svg

Danger

H315 - Veroorzaakt huidirritatie.
H317 - Kan een allergische huidreactie veroorzaken.
H320 - Veroorzaakt oogirritatie.
H332 - Schadelijk bij inademing.
H334 - Kan bij inademing allergie- of astmasymptomen of ademhalingsmoeilijkheden veroorzaken.
€ 206,23

(€ 170,44 zonder 21% btw)

Op voorraad

Beschrijving

Simpact™ 60A urethane is a low odor, fast-setting urethane elastomers which offers very high tear strength, impact resistance and wear resistance. Simpact™ urethanes are phthalate free, mercury free and MOCA free. Simpact™ urethanes pour easily. Working time is 4 minutes, handling time is 2 hours and full cure time is 48 hours at room temperature.Cured rubber has exceptional performance characteristics and dimensional stability. Simpact™ urethanes can be colored with SO-Strong™, UVO™ or Ignite™ colorants. Simpact™ urethanes are suitable for making impact resistant props, prototypes and display piecesMix Ratio 1A:1B - Shore Hardness 60 A - Elongation @ Break 400 % - Color White - Pot Life 4 minutes - Mix Ratio By Weight 100A:94B - Handling Time 2 hours - Cure Time 48 h 00

Instructies

Specificaties

Hundred Percent Modulus 312 psi
Color White
Mixed Viscocity 1,100 cps
Cure Time 48 hours
Pot Life 4 minutes
Specific Volume 25.7 cu. in./lb.
Die C Tear Strength 142 pli
Specific Gravity 1.08 g/cc
Mix Ratio By Weight 100A:94B
Shrinkage <.007 in. / in.
Mix Ratio By Volume 1A:1B
Tensile Strength 990 psi
Elongation At Break 400 %
Shore A Hardness 60
Handling Time 2 hours
Beschikbaar in Polyurethane Elastomer
Product Handling Time Cure Time Shore A Hardness Specific Gravity Specific Volume Tensile Strength Shrinkage Die C Tear Strength Elongation At Break Hundred Percent Modulus Mixed Viscocity Mix Ratio By Volume Mix Ratio By Weight Pot Life Hundred Percent Modulus Color Mixed Viscocity Cure Time Pot Life Specific Volume Die C Tear Strength Specific Gravity Mix Ratio By Weight Shrinkage Mix Ratio By Volume Tensile Strength Elongation At Break Shore A Hardness Handling Time
Simpact™ 80A II - - - - - - - - - - - - - - - - - - - - - - - - - - - - -
Simpact™ 60A 2 h. 48 h. 60 1.08 g/cc 25.7 cu. in./lb. 990 psi <.007 in. / in. 142 pli 400 % 312 psi 1,100 cps 1A:1B 100A:94B 4 min. 312 psi White 1,100 cps 48 h. 4 min. 25.7 cu. in./lb. 142 pli 1.08 g/cc 100A:94B <.007 in. / in. 1A:1B 990 psi 400 % 60 2 h.
Simpact™ 85A 2 h. 48 h. 85 1.09 g/cc 25.4 cu. in./lb. 1,573 psi <.007 in. / in. 182 pli 164 % 1,213 psi 1,100 cps - 85A:100B 4 min. 1,213 psi Off White 1,100 cps 48 h. 4 min. 25.4 cu. in./lb. 182 pli 1.09 g/cc 85A:100B <.007 in. / in. - 1,573 psi 164 % 85 2 h.

Waarom kopen bij FormX?

Schrijf je in voor onze nieuwsbrief

Ontvang € 5,- korting op je eerste aankoop!

Visa logo iDeal logo Mastercard logo Paypal logo FedEx logo FedEx logo
Deze website is ontwikkeld door Usecue B.V.
© 2026 FormX B.V.