TASK™ 16

Task16x ⓘ 85B5C341-D9E4-C14C-93EC-57A3EFD38962
Polyurethane Resin
exclamation.svg health-hazard.svg

Danger

H317 - Kan een allergische huidreactie veroorzaken.
H315 - Veroorzaakt huidirritatie.
€ 303,61

(€ 250,92 zonder 21% btw)

Niet op voorraad

Beschrijving

TASK™16 is a low odor, fast-setting Shore 80A/30D urethane that offers very high tear strength, impact resistance and wear resistance. TASK™16 is phthalate free, mercury free and MOCA free. Mixed one part A to two parts B by weight, TASK™16 pours easily. Working time is 6 minutes and handling time is 90 minutes at room temperature. Cured rubber has exceptional performance characteristics and dimensional stability. TASK™16 can be colored with SO‑Strong™ or Ignite™ colorants.TASK™16 is suitable for making fast mechanical parts, gaskets, wheels and pullies, impact resistant props, and archival master models. It is also used to make fast, wear resistant rubber molds for casting concrete or concrete stamping pads. TASK™16 is also an excellent choice for rotocasting to create hollow semi-rigid castings.IMPORTANT: Cured TASK™16 will inhibit the cure of liquid platinum silicone. You can not pour platinum silicone into cured TASK™16. Tin silicone must be used if you intend to pour silicone against cured TASK™16

Instructies

Specificaties

Hundred Percent Modulus 855 psi
Color Light Yellow
Mixed Viscocity 1,400 cps
Cure Time 24 hours
Pot Life 6 minutes
Specific Volume 25.64 cu. in./lb.
Die C Tear Strength 197 pli
Specific Gravity 1.08 g/cc
Mix Ratio By Weight 1A:2B
Shrinkage 0.0025 in. / in.
Tensile Strength 2,264 psi
Elongation At Break 233 %
Shore A Hardness 80
Shore D Hardness 30
Handling Time 90 minutes
Beschikbaar in Polyurethane Resin
Product Cure Time Specific Gravity Specific Volume Tensile Strength Tensile Modulus Compressive Strength Compressive Modulus Flexural Strength Shrinkage Heat Deflection Temp Elongation At Break Flexural Modulus Mixed Viscocity Mix Ratio By Volume Mix Ratio By Weight Pot Life Shore D Hardness Color Mixed Viscocity Cure Time Pot Life Flexural Strength Flexural Modulus Specific Volume Specific Gravity Mix Ratio By Weight Shrinkage Mix Ratio By Volume Tensile Strength Elongation At Break Shore D Hardness Heat Deflection Temp Compressive Strength Tensile Modulus Compressive Modulus Handling Time Handling Time Heat Deflection With Post Cure Heat Deflection With Post Cure Shore A Hardness Die C Tear Strength Hundred Percent Modulus Hundred Percent Modulus Die C Tear Strength Shore A Hardness
TASK™ 2 60 min. 1.12 g/cc 24.7 cu. in./lb. 6,650 psi 290,000 psi 8,300 psi 78,000 psi 9,500 psi 0.005 in. / in. 134 °F 6 % 288,000 psi 150 cps 1A:1B 115A:100B 7 min. 80 White 150 cps 60 min. 7 min. 9,500 psi 288,000 psi 24.7 cu. in./lb. 1.12 g/cc 115A:100B 0.005 in. / in. 1A:1B 6,650 psi 6 % 80 134 °F 8,300 psi 290,000 psi 78,000 psi - - - - - - - - - -
TASK™ 3 90 min. 1.12 g/cc 24.7 cu. in./lb. 6,650 psi 290,000 psi 8,300 psi 78,000 psi 9,500 psi 0.0025 in. / in. 134 °F 6 % 288,000 psi 150 cps 1A:1B 115A:100B 20 min. 80 White 150 cps 90 min. 20 min. 9,500 psi 288,000 psi 24.7 cu. in./lb. 1.12 g/cc 115A:100B 0.0025 in. / in. 1A:1B 6,650 psi 6 % 80 134 °F 8,300 psi 290,000 psi 78,000 psi - - - - - - - - - -
TASK™ 4 16 h. 1.167 g/cc 23.9 cu. in./lb. 6,500 psi 130,000 psi 7,400 psi 75,000 psi 9,000 psi 0.0035 in. / in. 110 °F 4 % 204,000 psi 250 cps - 100A:100B 20 min. 83 Ivory 250 cps 16 h. 20 min. 9,000 psi 204,000 psi 23.9 cu. in./lb. 1.167 g/cc 100A:100B 0.0035 in. / in. - 6,500 psi 4 % 83 110 °F 7,400 psi 130,000 psi 75,000 psi - - - - - - - - - -
TASK™ 5 24 h. 1.1 g/cc 25.2 cu. in./lb. 4,530 psi 200,000 psi 6,700 psi 83,000 psi 6,480 psi 0.007 in. / in. 145 °F 5 % 216,000 psi 600 cps 1A:1B 1A:1B 3 min. 77 Tan 600 cps 24 h. 3 min. 6,480 psi 216,000 psi 25.2 cu. in./lb. 1.1 g/cc 1A:1B 0.007 in. / in. 1A:1B 4,530 psi 5 % 77 145 °F 6,700 psi 200,000 psi 83,000 psi 15 min. 15 min. - - - - - - - -
TASK™ 6 24 h. 1.07 g/cc 25.9 cu. in./lb. 5,200 psi 146,000 psi 5,570 psi 65,000 psi 6,200 psi 0.0031 in. / in. 162 °F 4 % 182,500 psi 800 cps 1A:1B 1A:1B 7 min. 75 Tan 800 cps 24 h. 7 min. 6,200 psi 182,500 psi 25.9 cu. in./lb. 1.07 g/cc 1A:1B 0.0031 in. / in. 1A:1B 5,200 psi 4 % 75 162 °F 5,570 psi 146,000 psi 65,000 psi 75 min. 75 min. - - - - - - - -
TASK™ 7 10 min. 1.2 g/cc 23.1 cu. in./lb. 3,390 psi 150,700 psi 5,140 psi 57,600 psi 5,450 psi 0.0111 in. / in. 131 °F 15.1 % 148,900 psi 200 cps 1A:1B 104A:100B 2.5 min. 73 Off-White 200 cps 10 min. 2.5 min. 5,450 psi 148,900 psi 23.1 cu. in./lb. 1.2 g/cc 104A:100B 0.0111 in. / in. 1A:1B 3,390 psi 15.1 % 73 131 °F 5,140 psi 150,700 psi 57,600 psi - - - - - - - - - -
TASK™ 8 15 min. 1.09 g/cc 25.4 cu. in./lb. 5,840 psi 246,000 psi 8,760 psi 77,400 psi 8,280 psi 0.01 in. / in. 194 °F 4 % 271,000 psi 100 cps 1A:1B 120A:100B 2.5 min. 80 Off-White 100 cps 15 min. 2.5 min. 8,280 psi 271,000 psi 25.4 cu. in./lb. 1.09 g/cc 120A:100B 0.01 in. / in. 1A:1B 5,840 psi 4 % 80 194 °F 8,760 psi 246,000 psi 77,400 psi - - 263 °F 263 °F - - - - - -
TASK™ 11 16 h. 1.12 g/cc 24.7 cu. in./lb. 2,500 psi - - - - 0.0024 in. / in. - 100 % - 2,000 cps - 100A:100B 20 min. 60 Translucent White 2,000 cps 16 h. 20 min. - - 24.7 cu. in./lb. 1.12 g/cc 100A:100B 0.0024 in. / in. - 2,500 psi 100 % 60 - - - - - - - - - - - - - -
TASK™ 12 16 h. 1.08 g/cc 26 cu. in./lb. 2,700 psi - - - - 0.001 in. / in. - 300 % - 2,400 cps - 100A:44B 20 min. 60 Clear Amber 2,400 cps 16 h. 20 min. - - 26 cu. in./lb. 1.08 g/cc 100A:44B 0.001 in. / in. - 2,700 psi 300 % 60 - - - - - - - - - - - - - -
TASK™ 13 20 min. 1.15 g/cc 24.1 cu. in./lb. 1,800 psi - - - - 0.005 in. / in. - 125 % - 800 cps - 100A:120B 3 min. 50 Black 800 cps 20 min. 3 min. - - 24.1 cu. in./lb. 1.15 g/cc 100A:120B 0.005 in. / in. - 1,800 psi 125 % 50 - - - - - - - - - - - - - -
TASK™ 14 45 min. 1.15 g/cc 24.1 cu. in./lb. 1,800 psi - - - - 0.0035 in. / in. - 125 % - 800 cps - 100A:120B 10 min. 50 Black 800 cps 45 min. 10 min. - - 24.1 cu. in./lb. 1.15 g/cc 100A:120B 0.0035 in. / in. - 1,800 psi 125 % 50 - - - - - - - - - - - - - -
TASK™ 15 1 h. 1.12 g/cc 24.7 cu. in./lb. 2,720 psi 126,000 psi 5,450 psi 60,000 psi 5,450 psi 0.0042 in. / in. 117 °F 20 % 170,000 psi 600 cps - 75A:100B 6 min. 75 Opaque White 600 cps 1 h. 6 min. 5,450 psi 170,000 psi 24.7 cu. in./lb. 1.12 g/cc 75A:100B 0.0042 in. / in. - 2,720 psi 20 % 75 117 °F 5,450 psi 126,000 psi 60,000 psi - - - - - - - - - -
TASK™ 16 24 h. 1.08 g/cc 25.64 cu. in./lb. 2,264 psi - - - - 0.0025 in. / in. - 233 % - 1,400 cps - 1A:2B 6 min. 30 Light Yellow 1,400 cps 24 h. 6 min. - - 25.64 cu. in./lb. 1.08 g/cc 1A:2B 0.0025 in. / in. - 2,264 psi 233 % 30 - - - - 90 min. 90 min. - - 80 197 pli 855 psi 855 psi 197 pli 80
TASK™ 18 16 h. 1.57 g/cc 17.6 cu. in./lb. 3,250 psi 514,000 psi 8,420 psi 97,300 psi 10,700 psi 0.0006 in. / in. 149 °F 1 % 86,000 psi 4,400 cps - 26A:100B 20 min. 88 Metal Gray 4,400 cps 16 h. 20 min. 10,700 psi 86,000 psi 17.6 cu. in./lb. 1.57 g/cc 26A:100B 0.0006 in. / in. - 3,250 psi 1 % 88 149 °F 8,420 psi 514,000 psi 97,300 psi - - - - - - - - - -
TASK™ 21 1 h. 1.07 g/cc 25.9 cu. in./lb. 5,500 psi 270,000 psi 7,100 psi 78,500 psi 7,100 psi 0.0058 in. / in. 144 °F 7.5 % 250,000 psi 500 cps 2A:1B 2A:1B 6 min. 75 White 500 cps 1 h. 6 min. 7,100 psi 250,000 psi 25.9 cu. in./lb. 1.07 g/cc 2A:1B 0.0058 in. / in. 2A:1B 5,500 psi 7.5 % 75 144 °F 7,100 psi 270,000 psi 78,500 psi - - - - - - - - - -

Waarom kopen bij FormX?

Schrijf je in voor onze nieuwsbrief

Ontvang € 5,- korting op je eerste aankoop!

Visa logo iDeal logo Mastercard logo Paypal logo FedEx logo FedEx logo
Deze website is ontwikkeld door Usecue B.V.
© 2026 FormX B.V.