URE‑FIL™

Beschrijving

URE-FIL™ 17 pure aluminum pellet fillers can be used with Smooth-On® liquid epoxy and urethane resins to improve thermal conductivity, dimensional stability, reduce shrinkage in large mass castings, etc. These fillers can also be used to add evenly distributed weight to metal cold-castings and to create artistic casting effects.URE-FIL™ 17 are small grain aluminum pellets 400 micron. Smaller grain pellets will settle into areas of detail better, reducing voids between particles. FEATURES- Can be added to aluminum-filled urethane and epoxy resins for vacuum forming applications to increase thermal conductivity (even heat distribution) when casting parts for applications with higher temperature requirements.- Will add evenly distributed weight to metal cold-castings to simulate the feel of solid metal reproductions at a reduced expense compared to metal foundry castings.- Will lower exothermic (heat) temperatures during cure cycle (see chart on reverse side), which reduces the shrinkage rate resulting in improved dimensional stability in large mass castings.- Can be added to liquid urethane and epoxy resins to create metallic visual effects when used with clear and colored liquid plastics.- When fully cured, resin filled with URE-FIL™ 17 & 19 can be cut, drilled, turned and machine tooled.- Should not be used as fillers in RTV rubber products.

Instructies

Specificaties

URE-FIL 3 Mix Ratio	1A:1B:1 part URE-FIL 3
URE-FIL 5 Mix Ratio	1 part filler with 1A:1B Smooth-Cast 320 resin
URE-FIL 7 Maximum Mix Ratio	1A:1B:2 parts filler
URE-FIL 7 Trowelable Mix Ratio	1A:1B:3 parts filler
URE-FIL 9 Oven Temperature For Moisture Removal	150°F / 60°C
URE-FIL 9 Oven Time For Moisture Removal	4 hours
URE-FIL 9 Thickness For Moisture Removal	0.95 cm - 1.25 cm

Product	URE-FIL 3 Mix Ratio	URE-FIL 5 Mix Ratio	URE-FIL 7 Maximum Mix Ratio	URE-FIL 7 Trowelable Mix Ratio	URE-FIL 9 Oven Temperature For Moisture Removal	URE-FIL 9 Oven Time For Moisture Removal	URE-FIL 9 Thickness For Moisture Removal	Storage Temperature	Recommended Mix Ratio By Volume	Baking Temperature For Moisture Removal	Baking Time For Moisture Removal	Particle Thickness For Baking
URE‑FIL™	1A:1B:1 part URE-FIL 3	1 part filler with 1A:1B Smooth-Cast 320 resin	1A:1B:2 parts filler	1A:1B:3 parts filler	150°F / 60°C	4 h.	0.95 cm - 1.25 cm	-	-	-	-	-
Quarry Tone™ Fillers	-	-	-	-	-	-	-	73°F/23°C	1A + 1B + 2 Parts Powder Filler	150°F/60°C	4 h.	0.6 cm

Product

URE-FIL 3 Mix Ratio

URE-FIL 5 Mix Ratio

URE-FIL 7 Maximum Mix Ratio

URE-FIL 7 Trowelable Mix Ratio

URE-FIL 9 Oven Temperature For Moisture Removal

URE-FIL 9 Oven Time For Moisture Removal

URE-FIL 9 Thickness For Moisture Removal

Storage Temperature

Recommended Mix Ratio By Volume

Baking Temperature For Moisture Removal

Baking Time For Moisture Removal

Particle Thickness For Baking

URE‑FIL™

1A:1B:1 part URE-FIL 3

1 part filler with 1A:1B Smooth-Cast 320 resin

1A:1B:2 parts filler

1A:1B:3 parts filler

150°F / 60°C

4 h.

0.95 cm - 1.25 cm

Quarry Tone™ Fillers

73°F/23°C

1A + 1B + 2 Parts Powder Filler

150°F/60°C

4 h.

0.6 cm

Waarom kopen bij FormX?

Wij houden van materiaal

Al ruim dertig jaar zoeken we wereldwijd naar de beste materialen voor modelleren, mallen maken en gieten.

Inspirerend + Uniek

Van siliconen en harsen tot Jesmonite en special effects-materialen — een zorgvuldig samengesteld assortiment voor professionals, kunstenaars en makers.

Deskundig advies

Ons salesteam staat bekend om hun kennis en betrokkenheid en helpt je graag bij mallen maken, gieten, beeldhouwen en prototyping.

Verzending door heel Europa

We verzenden vanuit onze magazijnen in Amsterdam, Barcelona en Madrid naar klanten in heel Europa, van Griekenland tot Noorwegen.

Amsterdams origineel

Opgericht in Amsterdam groeide FormX van een lokale kunstgieterij uit tot een grote Europese leverancier — met onze wortels stevig in de stad.

URE‑FIL™

Beschrijving

Instructies

Specificaties