Shell Shock™ FAST

ShellshockFastx ⓘ A8518CA4-AD3E-A349-AE7C-3DAEE4629982
Polyurethane Resin
exclamation.svg health-hazard.svg

Danger

H315 - Veroorzaakt huidirritatie.
H317 - Kan een allergische huidreactie veroorzaken.
H320 - Veroorzaakt oogirritatie.
H332 - Schadelijk bij inademing.
H334 - Kan bij inademing allergie- of astmasymptomen of ademhalingsmoeilijkheden veroorzaken.
€ 136,85

(€ 113,10 zonder 21% btw)

Op voorraad

Beschrijving

Shell ShockTM is a thixotropic plastic that self thickens when mixed and can be brushed onto a variety of surfaces or into rubber molds. When Parts A and B are mixed in proper proportion (1A:3B by volume or 1A:5B by weight), material cures at room temperature with virtually no shrinkage to a hard, durable plastic that exhibits good compressive and flexural strength. Fully cured castings are rigid and can be sanded, primed and painted. Color effects are possible by adding SO-Strong Color Tints. Shell ShockTM is ideal for making fast, lightweight rigid molds for creating silicone appliances and effects (use as a replacement for ‘stone molds'). You can also brush a "gel coat" into a rubber mold and back it up with rigid foam, creating a highly detailed lightweight casting. This product can also be brushed onto styrofoam (polystyrol) as an impact resistant coating that can be sanded, primed and painted (minimum 3 coats recommended). Shell Shock can also be used to make rigid support shells for brush on rubber molds.

Instructies

Specificaties

Color Beige
Mixed Viscocity 3,000 cps
Cure Time 60 minutes
Pot Life 3 minutes
Flexural Strength 7,150 psi
Flexural Modulus 980,000 psi
Specific Volume 17.3 cu. in./lb.
Specific Gravity 1.60 g/cc
Mix Ratio By Weight 1A:5B
Shrinkage 0.0006 in. / in.
Mix Ratio By Volume 1A:4B
Tensile Strength 3,100 psi
Elongation At Break 0.4 %
Shore D Hardness 85
Heat Deflection Temp 135 °F
Compressive Strength 9,000 psi
Tensile Modulus 435,000 psi
Compressive Modulus 500,000 psi
Beschikbaar in Polyurethane Resin
Product Cure Time Specific Gravity Specific Volume Tensile Strength Tensile Modulus Compressive Strength Compressive Modulus Flexural Strength Shrinkage Heat Deflection Temp Elongation At Break Flexural Modulus Mixed Viscocity Mix Ratio By Volume Mix Ratio By Weight Pot Life Shore D Hardness Color Mixed Viscocity Cure Time Pot Life Flexural Strength Flexural Modulus Specific Volume Specific Gravity Mix Ratio By Weight Shrinkage Mix Ratio By Volume Tensile Strength Elongation At Break Shore D Hardness Heat Deflection Temp Compressive Strength Tensile Modulus Compressive Modulus
Shell Shock™ FAST 60 min. 1.60 g/cc 17.3 cu. in./lb. 3,100 psi 435,000 psi 9,000 psi 500,000 psi 7,150 psi 0.0006 in. / in. 135 °F 0.4 % 980,000 psi 3,000 cps 1A:4B 1A:5B 3 min. 85 Beige 3,000 cps 60 min. 3 min. 7,150 psi 980,000 psi 17.3 cu. in./lb. 1.60 g/cc 1A:5B 0.0006 in. / in. 1A:4B 3,100 psi 0.4 % 85 135 °F 9,000 psi 435,000 psi 500,000 psi
Shell Shock™ SLOW 5 h. 1.60 g/cc 17.3 cu. in./lb. 3,100 psi 435,000 psi 9,000 psi 500,000 psi 7,150 psi 0.0006 in. / in. 135 °F 0.4 % 980,000 psi 3,000 cps 1A:4B 1A:5B 8 min. 85 Beige 3,000 cps 5 h. 8 min. 7,150 psi 980,000 psi 17.3 cu. in./lb. 1.60 g/cc 1A:5B 0.0006 in. / in. 1A:4B 3,100 psi 0.4 % 85 135 °F 9,000 psi 435,000 psi 500,000 psi

Waarom kopen bij FormX?

Schrijf je in voor onze nieuwsbrief

Ontvang € 5,- korting op je eerste aankoop!

Visa logo iDeal logo Mastercard logo Paypal logo FedEx logo FedEx logo
Deze website is ontwikkeld door Usecue B.V.
© 2026 FormX B.V.