Smooth-Cast™ ONYX™

OnyxFastx ⓘ F8AB7487-AEC7-4549-BDDD-37609C6C69D4
Polyurethane Resin
Maat
1 kg 7.48 kg
Custom Property
fast slow
exclamation.svg health-hazard.svg

Danger

H315 - Veroorzaakt huidirritatie.
H317 - Kan een allergische huidreactie veroorzaken.
H320 - Veroorzaakt oogirritatie.
H332 - Schadelijk bij inademing.
H334 - Kan bij inademing allergie- of astmasymptomen of ademhalingsmoeilijkheden veroorzaken.
€ 182,60

(€ 150,91 zonder 21% btw)

Op voorraad

Beschrijving

Smooth-Cast ONYX® is a mercury-free urethane resin that cures quickly at room temperature to a deep black, solid plastic. ONYX® offers the convenience of a 1A:1B by volume mix ratio and has a very low viscosity, so it is easy to mix and pour. ONYX® has an ultimate shore hardness of 80D and offers higher physical properties and higher heat resistance vs. other general purpose resins.Advantages that ONYX® offers over other resins; If you desire a black casting, adding color pigment is not necessary Cured plastic is ultra-black and darker than competitive black resins Cured ONYX® plastic can be polished and buffed to a high gloss shine ONYX® offers higher heat resistance (to 200°F /94° C at room temperature) vs. competitive black resins Unlike other black resins, ONYX®does not contain mercury ONYX® is less expensive vs. other black resins.Applications include reproducing sculpture, making prototypes and potting / encapsulation. Because ONYX® is a fast curing resin and becomes hard quickly, it is also great for doing fast cold cast bronze, brass, copper, nickel/silver, etc.

Instructies

Beschikbaar in Polyurethane Resin
Product Handling Time Cure Time Specific Gravity Specific Volume Shrinkage Mixed Viscocity Mix Ratio By Volume Pot Life Shore D Hardness Color Mixed Viscocity Cure Time Pot Life Specific Volume Specific Gravity Shrinkage Mix Ratio By Volume Shore D Hardness Handling Time Tensile Modulus Compressive Strength Compressive Modulus Flexural Strength Heat Deflection Temp Elongation At Break Ultimate Tensile Flexural Modulus Flexural Strength Flexural Modulus Ultimate Tensile Elongation At Break Heat Deflection Temp Compressive Strength Tensile Modulus Compressive Modulus Mix Ratio By Weight Mix Ratio By Weight
SMASH! Plastic™ 90 min. 16 h. 1.036 g/cc 26.7 cu. in./lb. 0.0001 in. / in. 900 cps 1A:1B 5 min. 80 Clear 900 cps 16 h. 5 min. 26.7 cu. in./lb. 1.036 g/cc 0.0001 in. / in. 1A:1B 80 90 min. - - - - - - - - - - - - - - - - - -
Feather Lite™ - 2 h. 0.67 g/cc 41.3 cu. in./lb. 0.003 in. / in. 410 cps 1A:1B 8.5 min. 58 Beige 410 cps 2 h. 8.5 min. 41.3 cu. in./lb. 0.67 g/cc 0.003 in. / in. 1A:1B 58 - 156,000 psi 3,070 psi 53,700 psi 3,440 psi 140 °F 1.6 % 2,160 psi 164,300 psi 3,440 psi 164,300 psi 2,160 psi 1.6 % 140 °F 3,070 psi 156,000 psi 53,700 psi - -
Plasti-Paste™ II 90 min. 24 h. 1.0 g/cc 27.73 cu. in./lb. 0.005 in. / in. Paste 1A:2B 10 min. 70 Off White Paste 24 h. 10 min. 27.73 cu. in./lb. 1.0 g/cc 0.005 in. / in. 1A:2B 70 90 min. 235,000 psi 4,980 psi 62,700 psi 3,840 psi 130 °F 1.14 % 2,150 psi 203,000 psi 3,840 psi 203,000 psi 2,150 psi 1.14 % 130 °F 4,980 psi 235,000 psi 62,700 psi 62A:100B 62A:100B
Axsson - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - -
Smooth-Cast™ ONYX™ - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - -

Waarom kopen bij FormX?

Schrijf je in voor onze nieuwsbrief

Ontvang € 5,- korting op je eerste aankoop!

Visa logo iDeal logo Mastercard logo Paypal logo FedEx logo FedEx logo
Deze website is ontwikkeld door Usecue B.V.
© 2026 FormX B.V.